Subject:
HASL Tin-Lead component in thin coating
From:
Le Dai Tri <[log in to unmask]>
Date:
Tue, 9 May 2000 15:16:19 +0700
Content-Type:
multipart/alternative; boundary="----=_NextPart_000_0075_01BFB9C9.871182A0"
MIME-Version:
1.0
Reply-To:
"TechNet E-Mail Forum." <[log in to unmask]>, Le Dai Tri <[log in to unmask]>
Parts/Attachments:
text/plain (726 bytes) , text/html (2552 bytes) 
TechNeter,

We use horizontal HASL machine. When I measured the thickness of tin/lead 
    if the thickness was over 1um, the component of tin was 64~69%, 
    if the thickness was under 1um (0.8~0.9um), the component of tin was always over 70%. 
    (Tin/lead made-up in solder pot was 63+/-3%; 37+/-3%; board thicness was 1.6mm)
I did'nt know the reason why? 

In the case of component of tin was over 70%, what will happen in 
PCB Assembly manufacturing?

Any help would be appreciated.

Best regards,
Tri'.