TECHNET Archives

June 2008

TechNet@IPC.ORG

Options: Use Monospaced Font
Show Text Part by Default
Condense Mail Headers

Message: [<< First] [< Prev] [Next >] [Last >>]
Topic: [<< First] [< Prev] [Next >] [Last >>]
Author: [<< First] [< Prev] [Next >] [Last >>]

Print Reply
Sender:
X-To:
TechNet E-Mail Forum <[log in to unmask]>, Luan Nguyen <[log in to unmask]>
Date:
Thu, 26 Jun 2008 13:28:22 +0200
Reply-To:
TechNet E-Mail Forum <[log in to unmask]>, Hernefjord Ingemar <[log in to unmask]>
Subject:
From:
Hernefjord Ingemar <[log in to unmask]>
Content-Transfer-Encoding:
quoted-printable
In-Reply-To:
Content-Type:
text/plain; charset="us-ascii"
MIME-Version:
1.0
Parts/Attachments:
text/plain (72 lines)
When you place the tip on your component or solder site, the temperature
falls asymptotically from your 380 C or 425 C to the desired soldering
temperature, that can be 220 C or 240 C.  However, there are risks with
using as high temperature. If the component has a poor contact with the
solder site, the component (or part of it) may rush to 425 C in a few
seconds, and not all components like that. There may be a thermal
damage. If it's possible, use a lower temperature, and a tip with a
large mass, i.e. the temperature will not fall below 220 C or 240 C.

my 2 tips

Inge

 

-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of Luan Nguyen
Sent: den 26 juni 2008 10:48
To: [log in to unmask]
Subject: [TN] Temperature of lead-free for hand soldering

Dear All,
We have a question about set temperature for hand soldering. We were
using Hakko FM-202.
- For tin lead, we set 320 C degree
- For lead-free, we plan to set 380 C degree. However, we can not find
any standard (IPC, J-STD) mention to set temperature. We refer some
documents, experience sharing that temperature range is from 370 C
degree to 425 C degree. Moreover, in there is also mention as "> 80 W
hand soldering is always OK" that effect us due to Hakko FM-202 have
power consumption of soldering iron is 70W.

Please help me any reference, any document, any advice.

Thanks and best regards,


***************************
Nguyen Hoang Luan
QC&Training Supervisor
Spartronics VietNam Co, Ltd.
No.3, Street No.6, VSIP
Th An Dist., BDuong Prov., VN
Tel: (84-650) 784 890
Fax: (84-650) 784 891
Mobile: 090.3.667448
Email: [log in to unmask]
***************************

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0 To
unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet To temporarily halt or
(re-start) delivery of Technet send e-mail to [log in to unmask]: SET
Technet NOMAIL or (MAIL) To receive ONE mailing per day of all the
posts: send e-mail to [log in to unmask]: SET Technet Digest Search the
archives of previous posts at: http://listserv.ipc.org/archives Please
visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for
additional information, or contact Keach Sasamori at [log in to unmask] or
847-615-7100 ext.2815
-----------------------------------------------------

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------

ATOM RSS1 RSS2