Mark,
IMHO, there will be no problem as long as the underlying copper was
correctly prepared before hassling it. Your spec. allows a good
tolerance beyond the limits.
Brian
Mark Hargreaves wrote:
>
> Hi All,
> Our most recent HAL solder analysis report showed tin at 61.17% (report
> spec is 61.5 - 63.5) and gold at 0.055% (report spec is 0.045%).
> We're replacing the solder, but I'm wondering about the solderability of
> boards that have already been processed. Will these levels not, possibly,
> or certainly cause soldering problems?
>
> Thanks,
> Mark
>
> ---------------------------------------------------------------------------------
> Technet Mail List provided as a free service by IPC using LISTSERV 1.8d
> To unsubscribe, send a message to [log in to unmask] with following text in
> the BODY (NOT the subject field): SIGNOFF Technet
> To temporarily halt delivery of Technet send the following message: SET Technet NOMAIL
> Search previous postings at: www.ipc.org > On-Line Resources & Databases > E-mail Archives
> Please visit IPC web site (http://www.ipc.org/html/forum.htm) for additional
> information, or contact Keach Sasamori at [log in to unmask] or 847-509-9700 ext.5315
> ---------------------------------------------------------------------------------
---------------------------------------------------------------------------------
Technet Mail List provided as a free service by IPC using LISTSERV 1.8d
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt delivery of Technet send the following message: SET Technet NOMAIL
Search previous postings at: www.ipc.org > On-Line Resources & Databases > E-mail Archives
Please visit IPC web site (http://www.ipc.org/html/forum.htm) for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-509-9700 ext.5315
---------------------------------------------------------------------------------
|
|
|