Hi Joyce,
I have always argued that the word 'embrittlement' was not a good descriptor for the phenomenon.
Werner
-----Original Message-----
From: Joyce Koo <[log in to unmask]>
To: TechNet E-Mail Forum <[log in to unmask]>; [log in to unmask]
Sent: Wed, 15 Apr 2009 5:11 pm
Subject: RE: [TN] Gold/Tin Intermetallics, why are we afraid?
"ImAG finishes have a 12-month shelf life in a controlled environment
(<35[degrees]C/<85[degrees] RH), which can be significantly shortened
when exposed to air pollution with high sulfur and chlorine content.
Silver embrittlement Embrittlement
A general set of phenomena whereby materials suffer a marked decrease in
their ability to deform (loss of ductility) or in their ability to
absorb energy during fracture (loss of toughness), with little change in
other mechanical properties, such ([Ag.sub.3]Sn intermetallics) of
solder joints may occur when the finish thickness exceeds IPC-4553
recommendations and Pb-free, high silver content solders are used. ImAG
is not recommended for high-reliability assemblies that must meet
IPC-6010 Class 3 requirements, but is acceptable for Classes 1 and 2."
http://www.thefreelibrary.com/Will+discoloration+tarnish+ImAg+reliabilit
y%3F+Watch+for+silver...-a0193896272
-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of Werner Engelmaier /*
Sent: Wednesday, April 15, 2009 4:34 PM
To: [log in to unmask]
Subject: Re: [TN] Gold/Tin Intermetallics, why are we afraid?
Hi Vlad,
I cannot comment on your specific case, but look at the pics below to
see
Ag-embrittlement.
Sorry 'Netters, IPC strips pics.
Werner
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text
in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to
[log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to
[log in to unmask]: SET Technet Digest
Search the archives of previous posts at:
http://listserv.ipc.org/archives
Please visit IPC web site
http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100
ext.2815
-----------------------------------------------------
---------------------------------------------------------------------
This transmission (including any attachments) may contain confidential
information, privileged material (including material protected by the
solicitor-client or other applicable privileges), or constitute non-public
information. Any use of this information by anyone other than the intended
recipient is prohibited. If you have received this transmission in error, please
immediately reply to the sender and delete this information from your system.
Use, dissemination, distribution, or reproduction of this transmission by
unintended recipients is not authorized and may be unlawful.
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------
|