TECHNET Archives

August 1999

TechNet@IPC.ORG

Options: Use Monospaced Font
Show Text Part by Default
Condense Mail Headers

Message: [<< First] [< Prev] [Next >] [Last >>]
Topic: [<< First] [< Prev] [Next >] [Last >>]
Author: [<< First] [< Prev] [Next >] [Last >>]

Print Reply
Content-Type:
text/plain
Sender:
Subject:
From:
Doug Black <[log in to unmask]>
Date:
Tue, 17 Aug 1999 09:11:00 +0100
MIME-Version:
1.0
X-To:
"Martin, Jesse" <[log in to unmask]>
Reply-To:
"TechNet E-Mail Forum." <[log in to unmask]>, Doug Black <[log in to unmask]>
Parts/Attachments:
text/plain (74 lines)
Martin,

        In my experience the problem with the solder paste building up on
the underside of the stencil is initially caused by poor gasket of stencil
to board. This can either be due to poorly finished PCB's or oversize or
poorly defined apertures.

        With regard to your underside cleaning issues, sometines the solvent
used in the  underside cleaning unit can have an adverse effect in drying
out the small quantity of solder paste on the underside of the stencil  very
quickly. This accompanied by poor undersceen cleaning performance can result
in a very quick build up of solder paste.

        The best advice I can offer is to look at the optimisation of the
underscreen cleaning unit including the paper being used and the solvent in
the tank. The other area to look at would be the gasketing of the board
against the PCB. Look at the aperture size and finish in the stencil. Have
the apertures been reduced correctly in line with the PCB pads?

I hope this is of some help.

If I can be of any further assistance please do not hesitate to contact me.

Doug Black
Technical Manager
Dek Precision Screens Division
Dek Printign Machines Ltd.
e-mail: [log in to unmask]
 ----------
From: Martin, Jesse
To: [log in to unmask]
Subject: [TN] Solder paste stencils
Date: 16 August 1999 20:08

Has anyone had a problem with solder paste stencils that have a build up of
solder paste on the bottom (PCB) side of the stencil that won't come off in
the stencil cleaner? I think what happens is the vacuum/paper wiper leaves
some on the bottom after each wipe and the more it wipes the harder it is to
get off. I can pop it off with an Xacto knife or the like but is very time
consuming. Only other thing that works is using a Scotchbrite pad but that
leaves a lot of scratches (which probably causes faster build up). Have also
tried stainless steel cleaner with no luck. We use an old Austin American
batch aqueous cleaner with saponifier at 120 degrees F. Any and all ideas
welcome.

##############################################################
TechNet Mail List provided as a free service by IPC using LISTSERV 1.8c
##############################################################
To subscribe/unsubscribe, send a message to [log in to unmask] with following
text in
the body:
To subscribe:   SUBSCRIBE TECHNET <your full name>
To unsubscribe:   SIGNOFF TECHNET
##############################################################
Please visit IPC web site (http://www.ipc.org/html/forum.htm) for additional
information.
If you need assistance - contact Gayatri Sardeshpande at [log in to unmask] or
847-509-9700 ext.5365
##############################################################

##############################################################
TechNet Mail List provided as a free service by IPC using LISTSERV 1.8c
##############################################################
To subscribe/unsubscribe, send a message to [log in to unmask] with following text in
the body:
To subscribe:   SUBSCRIBE TECHNET <your full name>
To unsubscribe:   SIGNOFF TECHNET
##############################################################
Please visit IPC web site (http://www.ipc.org/html/forum.htm) for additional
information.
If you need assistance - contact Gayatri Sardeshpande at [log in to unmask] or
847-509-9700 ext.5365
##############################################################

ATOM RSS1 RSS2