Typical 100-200 uin depending on the surface roughness of CuBe. The smoother
the low the Ni. Au should be porious in not the Ni must be smooth.
Richard Haynes
609-497-4584
-----Original Message-----
From: Henry Kruckeberg <[log in to unmask]>
To: [log in to unmask] <[log in to unmask]>
Date: Thursday, June 10, 1999 12:42 PM
Subject: [TN] Ni. Plating
>Does anyone have any info on the optimum Ni. thickness to prevent base
metal
>migration in a electro deposited AU. over Ni. on beryllium copper
application.
>
>Any input appreciated
>
>################################################################
>TechNet E-Mail Forum provided as a free service by IPC using LISTSERV 1.8c
>################################################################
>To subscribe/unsubscribe, send a message to [log in to unmask] with following
text in the body:
>To subscribe: SUBSCRIBE TechNet <your full name>
>To unsubscribe: SIGNOFF TechNet
>################################################################
>Please visit IPC's web site (http://www.ipc.org) "On-Line Services" section
for additional information.
>For technical support contact Hugo Scaramuzza at [log in to unmask] or
847-509-9700 ext.312
>################################################################
>
>
################################################################
TechNet E-Mail Forum provided as a free service by IPC using LISTSERV 1.8c
################################################################
To subscribe/unsubscribe, send a message to [log in to unmask] with following text in the body:
To subscribe: SUBSCRIBE TechNet <your full name>
To unsubscribe: SIGNOFF TechNet
################################################################
Please visit IPC's web site (http://www.ipc.org) "On-Line Services" section for additional information.
For technical support contact Hugo Scaramuzza at [log in to unmask] or 847-509-9700 ext.312
################################################################
|
|
|