Hi Don,
What type of solder paste are you using (water borne or alcohol based)?
Amount and type of residue left on the assy after reflow? Is this
residue flowing onto/into PTHs? Have you processed the assembly with TH
only to baseline a best case?
This additional info will help in determining possible solutions.
Thanks.
Steve
################################################################