Hi Pat -
We are using the Sn43/Pb43/Bi14 alloy on one product with very good
success. The low melting point helps avoid some thermal shock issues
we have on the assembly. One word of caution - the Sn43/Pb43/Bi14
alloy forms a low melting point at approximately 95 C which causes the
solder joints to fall apart. In our application the product never goes
above 80C in its use environment so the use of the Sn43/Pb43/Bi14
alloy is feasible. Take a look at your product in its use environment
with the temperature excursions in mind to see if you will or will not
have problems. I would also recommend that you set up a specific
soldering process around the alloy to prevent it from accidentally
"migrating" to other areas of the manufacturing process. Good Luck.
Dave Hillman
Rockwell Collins
[log in to unmask]
______________________________ Reply Separator _________________________________
Subject: ASSY: Sn43/Pb43/Bi14 solder
Author: [log in to unmask] at ccmgw1
Date: 7/9/97 8:43 AM
Hi there,
Is anynoby in PCB assemblers using Sn43/Pb43/Bi14 solder paste as primary
or secondary process (to reflow heavy components on double-sided PCBs)??
Is it enough reliable. Having in mind that is it a non-eutectic alloy , will
the rework be a challenge vs Sn63/Pb37 and how is the post-reflow inspection
? What is the recommended surface finish of the PCB to achieve proper
wetting results? Would HASL finish be acceptable to support or wett the
solder? Is there intermetallic formation at the joint Pb/Sn/Bi and HASL
finish? How is the strength between both?
I saw a article in the september 1996 publication of SMT MAGAZINE but I
need comments from assemblers. If you have any documentations or documented
works (qualification, reliability test results as thermal cycling, thermal
shock, humidity cycling and X-section & surface analysis for that alloy vs
Sn/Pb would be very appreciated.
I know that there is a lot of answers asked, thanks in advance for your
responses and your sharing.
Regards. =20
-------------------------------------------------
Patrick Ducas
Process Quality Engineer=20
Matrox Electronic Systems Ltd
E-mail: [log in to unmask]
T=E9l:(514)969-6000 ext.2971 Fax:(514)685-3415
-------------------------------------------------
=09
***************************************************************************
* TechNet mail list is provided as a service by IPC using SmartList v3.05 *
***************************************************************************
* To subscribe/unsubscribe send a message <to: [log in to unmask]> *
* with <subject: subscribe/unsubscribe> and no text in the body. *
***************************************************************************
* If you are having a problem with the IPC TechNet forum please contact *
* Dmitriy Sklyar at 847-509-9700 ext. 311 or email at [log in to unmask] *
***************************************************************************
***************************************************************************
* TechNet mail list is provided as a service by IPC using SmartList v3.05 *
***************************************************************************
* To subscribe/unsubscribe send a message <to: [log in to unmask]> *
* with <subject: subscribe/unsubscribe> and no text in the body. *
***************************************************************************
* If you are having a problem with the IPC TechNet forum please contact *
* Dmitriy Sklyar at 847-509-9700 ext. 311 or email at [log in to unmask] *
***************************************************************************
|
|
|