The unfused tin/lead finish was used very frequently in the 60's and 70's and
if cleaned and stored properly had good solderabability for wave solder
applications using RMA fluxes. I used the finish for at least 10 years with
good results. The only problem was tin/lead slivers and if you use tin, a
major problem is also tin slivers. The factory where I worked had a avg, RH
of 28% and both unfused tin/lead and unfused tin were used and boards were
stored an average of 6 months. The bright or semi bright unfused tin plates
have a good shelf life and In test that I have run were very satisfactory
after two years of storage. The sliver problem was usually alleviated by
building a slight mushroom with the copper and then plating the tin/lead
covering. over the mushroom so that there was no overhang of the tin/lead
that was not supported by copper.
As David mentioned, the use of a thin 0.0002-0.0003 in. of tin/lead plate as
a final finish is not infrequently used for surface mount to provide a flat
land and they are soldered with standard no-clean and RMA fluxes. Good
storage conditions, again, are desirable.
Phi Hinton
[log in to unmask]
***************************************************************************