Hey there technetters. A while back, I sent a message about enig plating
contamination in NON-plated holes. I've bounced it back to the board
shop saying that it is unacceptable, but they claim it is due to 6012
3.5.2
I also think it's unacceptable in the 4552 spec. The design
documentation clearly states non-plated. It's not plated, just partially
plated.
Any advice?
Thanks.
_____________________________________________________________________________________
Henry Rekers P. Eng | Schneider Electric | Global Supply Chain |
Senior Manufacturing Engineer
Phone: +1-250-652-7100 ext. 7510 | Toll Free: +1-866-466-7627 ext.
7510 | Fax: +1-250-544-2390 |
Email: [log in to unmask] | Site:
www.schneider-electric.com | Address: 2195 Keating Cross Road,
Saanichton, BC, Canada, V8M 2A5
*** Please consider the environment before printing this e-mail
______________________________________________________________________
This email has been scanned by the Symantec Email Security.cloud service.
For more information please contact helpdesk at x2960 or [log in to unmask]
______________________________________________________________________
|
|
|