What is the Au thickness? How may inserted is the plating rated for? Try XRF testing.
Victor,
-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of Ioan Tempea
Sent: Tuesday, October 23, 2012 7:41 AM
To: [log in to unmask]
Subject: [TN] Ni barrier thickness - Part II
Dear Technos,
I guess you had all already guessed where I'm trying to get at: I have Cu diffusion at the surface of the Au on some connecting pins and can't assess the effect on long term reliability.
So here comes the second question: are there any studies / rules of thumb that could say how much of the Au surface may be lost without any negative impact on the functionality? I definitely got the message that everything is application related, but just trying my luck...
Or, anybody has an idea how could I test the long term reliability in this situation?
Thanks,
Ioan Tempea, ing.
Ingénieur principal de fabrication / Senior Manufacturing Engineer [signature002]<http://www.digico.cc/>
950 RUE BERGAR, LAVAL, QC, H7L 5A1<http://g.co/maps/2gh3f>
T+ 1 (450) 967-7100, EXT244
------------------------------------------------------------------------
[signature001] <http://www.facebook.com/pages/Digico/277076778479>
------------------------------------------------------------------------
Lauréat Dunamis 2012<http://digico.cc/dunamis-2012/>
Entreprise manufacturière / Gestion du capital humain
______________________________________________________________________
This email has been scanned by the Symantec Email Security.cloud service.
For more information please contact helpdesk at x2960 or [log in to unmask] ______________________________________________________________________
______________________________________________________________________
This email has been scanned by the Symantec Email Security.cloud service.
For more information please contact helpdesk at x2960 or [log in to unmask]
______________________________________________________________________
|
|
|