TECHNET Archives

October 2008

TechNet@IPC.ORG

Options: Use Monospaced Font
Show Text Part by Default
Condense Mail Headers

Message: [<< First] [< Prev] [Next >] [Last >>]
Topic: [<< First] [< Prev] [Next >] [Last >>]
Author: [<< First] [< Prev] [Next >] [Last >>]

Print Reply
Sender:
X-To:
TechNet E-Mail Forum <[log in to unmask]>, [log in to unmask]
Date:
Mon, 6 Oct 2008 07:08:37 -0400
Reply-To:
TechNet E-Mail Forum <[log in to unmask]>, [log in to unmask]
Subject:
From:
"Randy Bock Sr." <[log in to unmask]>
In-Reply-To:
Content-Type:
text/plain; charset="US-ASCII"
MIME-Version:
1.0
Parts/Attachments:
text/plain (130 lines)
FYI  Works  ok for me. 


Randy Bock Sr.
Quality  Engineer
Enterprise Quality  Assurance
AddressRight Printers
(email)  [log in to unmask]
Newtown Building 2
203 270-4931  Ext
    8-426-4931  In
203 270-4982 Fax

This e-mail message may contain confidential, proprietary and/or 
privileged information.  It is intended only for the use of the intended 
recipient(s).  If you receive this in error, please immediately advise the 
sender by reply e-mail and delete this e-mail message.  Any disclosure, 
copying, distribution or use of the information contained in the e-mail to 
or by anyone other than the intended recipient is strictly prohibited. Any 
views expressed in this message are those of the individual sender, except 
when the sender specifically states them to be the views of the company. 
Thank You.



Victor Hernandez <[log in to unmask]> 
Sent by: TechNet <[log in to unmask]>
10/06/2008 07:05 AM
Please respond to
TechNet E-Mail Forum <[log in to unmask]>; Please respond to
[log in to unmask]


To
[log in to unmask]
cc

Subject
Re: [TN] Barrel and Corner cracks in copper electroplating






Unable to open files.

-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of Ido Mashall
Sent: Friday, October 03, 2008 1:13 PM
To: [log in to unmask]
Subject: [TN] Barrel and Corner cracks in copper elctroplating

 
Hello technet

We are suffering a serious problem of barrel and corner cracks in the
pattern copper plate bath.
Please look at the following pic. (all after 288C solder thermal stress)

http://www.drivehq.com/file/df.aspx/shareID4765976/fileID233954134/eo-d3
497-1.jpg
 
http://www.drivehq.com/file/df.aspx/shareID4765976/fileID233954135/es-c9
633-1.jpg
 
http://www.drivehq.com/file/df.aspx/shareID4765976/fileID233954138/as-d3
715.jpg

This very strange phenomenon occurs only in the second copper, and does
not occur in the panel plated copper.

After testing all bath components, they seem to be ok. CVS is oK, hull
cell is OK. It seems the copper lost its mechanical properties.

We are looking for possible contamination and changed the bath for a new
fresh bath, and it happens again after a few days..

Does somebody have some idea why this cracks can occur? What other
reasons..?


Thanks.


Ido Mashall


Fax: +972-4-6376666, Tel: +972-77-2127172, 

Mobile +972-52-5901114,  http://www.beyond-materials.com/index-en.htm

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0 To
unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet To temporarily halt or
(re-start) delivery of Technet send e-mail to [log in to unmask]: SET
Technet NOMAIL or (MAIL) To receive ONE mailing per day of all the
posts: send e-mail to [log in to unmask]: SET Technet Digest Search the
archives of previous posts at: http://listserv.ipc.org/archives Please
visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for
additional information, or contact Keach Sasamori at [log in to unmask] or
847-615-7100 ext.2815
-----------------------------------------------------

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to 
[log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to 
[log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 
for additional information, or contact Keach Sasamori at [log in to unmask] or 
847-615-7100 ext.2815
-----------------------------------------------------


---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------

ATOM RSS1 RSS2