We always have problems (both at assembly and more import
Peter,
We always have problems (both at assembly and more importantly with
reliability) when we use PtAg or PdPtAg terminated components. If you
can find another component that isn't terminated with one of these noble
metal terminations use the alternative.
Regards,
George
George M. Wenger
Andrew Corporation Wireless Network Solutions
Senior Principal FMA / Reliability Engineer
40 Technology Drive, Warren, NJ 07059
(908) 546-4531 [Office] (732) 309-8964 [Cell]
-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of Peter Barton
Sent: Wednesday, January 31, 2007 5:18 AM
To: [log in to unmask]
Subject: [TN] Soldering to Pt/Ag conponent terminations.
We are seeing unusual soldered joints when soldering to components with
Platinum/Silver metallised terminations. At the margin between the
bottom of
the component termination and the PCB surface there are a number of
blowholes in the bulk solder. There also appears to be poor wetting to
the
vertical end of the termination itself. All other solder joints on the
assembly in question are good, well wetted and on a number of other
plating
finishes.
The solder paste is SAC305 and the PCB finish is ENIG. Reflow is carried
out
in a vapour phase process with a maximum assembly temperature of 235
deg. C.
Time above liquidus (217 Deg C.) is around 50 seconds.
I have requested feedback from the component manufacturer but it's like
pulling teeth so in the meantime I an seeking your considered opinions.
Many thanks
-----------------------------------------------------------------------
Peter Barton
Senior Process Engineer
ACW Technology Ltd
Dinas Isaf West
Tonypandy
Mid Glamorgan. CF40 1XX Wales
Tel: 01443 425275 (direct)
Fax: 023 8048 4882
International Tel : +44 1443 425200
International Fax : +44 23 8048 4882
Website/URL: www.acw.co.uk
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text
in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to
[log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to
[log in to unmask]: SET Technet Digest
Search the archives of previous posts at:
http://listserv.ipc.org/archives
Please visit IPC web site
http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100
ext.2815
-----------------------------------------------------
------------------------------------------------------------------------------------------------
This message is for the designated recipient only and may
contain privileged, proprietary, or otherwise private information.
If you have received it in error, please notify the sender
immediately and delete the original. Any unauthorized use of
this email is prohibited.
------------------------------------------------------------------------------------------------
[mf2]
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------
|
|
|