Phil,
Copper content is 5.5 times higher that should be. 
Try to remove the excess copper by veeery slow cooling of your solder pot in
static conditions.Around 190 centigrade you should get the first dross on
the surface ,which is very rich in copper.Take it out.
Good luck
Edward

Edward Szpruch
Eltek , Manager of Process Engineering
P.O.Box 159 ; 49101 Petah Tikva Israel
Tel  ++972 3 9395050 , Fax  ++972 3 9309581
e-mail   [log in to unmask]

> -----Original Message-----
> From: Phil Nutting [SMTP:[log in to unmask]]
> Sent: â àåâåñè 14 2001 14:48
> To:   [log in to unmask]
> Subject:      [TN] Solder analysis results
> 
> Ok folks, here is today's question.
> 
> I just received a Certificate of Analysis (our first one) for the solder
> in our Soltec Waver Solder machine.  All parameters are "within
> specification" except the percentage of copper which is at 1.6859. (Tin
> is at 61.3% and Lead is at 36.99% and other stuff is at 0.0199%)  We run
> 63/37 in the wave.  We only solder our own product, none of which goes
> into "mission critical" applications.  We normally build our product to
> IPC-A-610C, Class 2.
> 
> My question is two-fold.  Should I worry about this?  If so, how do I
> fix it with 1700 pounds of solder in the solder pot? 
> 
> Thanks is advance for sharing your knowledge.
> 
> Phil Nutting
> Manufacturing Engineer
> Kaiser Systems, Inc.
> 
> --------------------------------------------------------------------------
> -------
> Technet Mail List provided as a free service by IPC using LISTSERV 1.8d
> To unsubscribe, send a message to [log in to unmask] with following text in
> the BODY (NOT the subject field): SIGNOFF Technet
> To temporarily halt delivery of Technet send the following message: SET
> Technet NOMAIL
> Search previous postings at: www.ipc.org > On-Line Resources & Databases >
> E-mail Archives
> Please visit IPC web site (http://www.ipc.org/html/forum.htm) for
> additional
> information, or contact Keach Sasamori at [log in to unmask] or 847-509-9700
> ext.5315
> --------------------------------------------------------------------------
> -------

---------------------------------------------------------------------------------
Technet Mail List provided as a free service by IPC using LISTSERV 1.8d
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt delivery of Technet send the following message: SET Technet NOMAIL
Search previous postings at: www.ipc.org > On-Line Resources & Databases > E-mail Archives
Please visit IPC web site (http://www.ipc.org/html/forum.htm) for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-509-9700 ext.5315
---------------------------------------------------------------------------------