TECHNET Archives

March 2013

TechNet@IPC.ORG
Options: Use Monospaced Font
Show Text Part by Default
Condense Mail Headers

Message: [<< First] [< Prev] [Next >] [Last >>]
Topic: [<< First] [< Prev] [Next >] [Last >>]
Author: [<< First] [< Prev] [Next >] [Last >>]

Print Reply
Sender:
TechNet <[log in to unmask]>
X-To:
TechNet E-Mail Forum <[log in to unmask]>, "[log in to unmask]" <[log in to unmask]>
Date:
Thu, 21 Mar 2013 09:56:30 -0500
Reply-To:
TechNet E-Mail Forum <[log in to unmask]>, "Giamis, Andy" <[log in to unmask]>
Message-ID:
<[log in to unmask]>
Subject:
Re: SAC 305 etch
From:
"Giamis, Andy" <[log in to unmask]>
MIME-Version:
1.0
In-Reply-To:
<[log in to unmask]>
Content-Transfer-Encoding:
quoted-printable
Content-Type:
text/plain; charset="us-ascii"
Parts/Attachments:
text/plain (26 lines) 
To see Sn grain boundaries , don't etch.  Use cross-polarizers.



-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of [log in to unmask]
Sent: Thursday, March 21, 2013 10:53 AM
To: [log in to unmask]
Subject: [TN] SAC 305 etch

What would a good etch be for etching SAC305 solder joints to enhance 
viewing grain boundaries?

Thanks,
John

______________________________________________________________________
This email has been scanned by the Symantec Email Security.cloud service.
For more information please contact helpdesk at x2960 or [log in to unmask] 
______________________________________________________________________

______________________________________________________________________
This email has been scanned by the Symantec Email Security.cloud service.
For more information please contact helpdesk at x2960 or [log in to unmask] 
______________________________________________________________________

ATOM RSS1 RSS2