TECHNET Archives

January 2008

TechNet@IPC.ORG

Options: Use Monospaced Font
Show Text Part by Default
Condense Mail Headers

Message: [<< First] [< Prev] [Next >] [Last >>]
Topic: [<< First] [< Prev] [Next >] [Last >>]
Author: [<< First] [< Prev] [Next >] [Last >>]

Print Reply
Sender:
X-To:
Date:
Wed, 16 Jan 2008 19:12:07 -0500
Reply-To:
TechNet E-Mail Forum <[log in to unmask]>, "Igoshev, Vladimir" <[log in to unmask]>
Subject:
MIME-Version:
1.0
Content-Transfer-Encoding:
base64
Content-Type:
text/plain; charset=utf-8
From:
"Igoshev, Vladimir" <[log in to unmask]>
Parts/Attachments:
text/plain (1 lines)
Bev,



The bulk concentration (particularly when you are talking about a ball, not a joint) means almost nothing.



It is important whether the platelets are segregated at the ball surface or they are in the bulk. 



Coming back to your original question, I'd have to say that all the answers you've got so far are right to some extent, but all of them should have started withqq a famous phrase "it depends" :-)



In addition, I think you should have asked whether a mixture/alloy of Sn and AuSn4 intermetallics is sokderable.



Let me explain.



If you try to solder to a surface covered with a Sn/ AuSn4 mixture (and the bulk concentration of Au in the mixture/alloy is less than 30%), then you have pure Sn in the mixture and the lower the bulk percentage of Au, the more pure Sn you have in the alloy. IF there is no segregation of the AuSn4 intermetallics at the surface, then the more pure Sn - the easier to solder to it. However, it the intermetallics is segregated at the free surface, then one would be trying to solder to it and according to the Werner's e-mail, it's a bad idea. 



Regards,



Vladimir



----- Original Message -----

From: TechNet <[log in to unmask]>

To: [log in to unmask] <[log in to unmask]>

Sent: Wed Jan 16 17:24:52 2008

Subject: Re: [TN] SV: [TN] SV: [TN] Solderability of Tin-Gold Intermetallic



Dave,

I only have 0.8 to 1.2% gold in the solder balls - as determined by XRF.

Bev



-----Original Message-----

From: TechNet [mailto:[log in to unmask]] On Behalf Of David D. Hillman

Sent: Wednesday, January 16, 2008 5:06 PM

To: [log in to unmask]

Subject: Re: [TN] SV: [TN] SV: [TN] Solderability of Tin-Gold Intermetallic



Hi gang! Steve - I just sent you another set of photos showing a solder 

joint that has gold embrittlement. Bev - if you have a solder joint that 

contains the AuSn4 microstructure phase then you have an indication that 

your overall composition has exceeded the "magical" 4% limit.  The 

presence of the AuSn4 platelets cause the solder joint to behave in a 

brittle manner when subjected to some use environments. The formation of 

the AuSn4 phase isn't going to interfere with the formation of your solder 

joint but they do result in solder joint integrity degradation. The 

pretinning of gold plated component leads is an attempt to replace the 

gold with a solder coating and lower the overall total percentage of gold 

that would exist in the solder joint - the lower the overall solder joint 

gold content, the lower the likelihood for the AuSn4 phase to form.



Dave Hillman

Rockwell Collins

[log in to unmask]









Steve Gregory <[log in to unmask]> 

Sent by: TechNet <[log in to unmask]>

01/16/2008 03:35 PM

Please respond to

TechNet E-Mail Forum <[log in to unmask]>; Please respond to

Steve Gregory <[log in to unmask]>





To

[log in to unmask]

cc



Subject

Re: [TN] SV: [TN] SV: [TN] Solderability of Tin-Gold Intermetallic













Hi Inge ol' pal!



I went back and looked on my pages, and am not sure if they're still 

there. But one of these might be:



http://stevezeva.homestead.com/files/fracture_bad.jpg



http://stevezeva.homestead.com/files/fracture_bad_2.jpg





Steve





 



-----Original Message-----

From: TechNet [mailto:[log in to unmask]] On Behalf Of Hfjord

Sent: Wednesday, January 16, 2008 3:09 PM

To: [log in to unmask]

Subject: [TN] SV: [TN] SV: [TN] Solderability of Tin-Gold Intermetallic



Not really true, the Scottish blood in my veines tells me to be careful 

with money, the kyrgise blood makes me crush the table, therefore, noone 

can actually be under it. 



I think there are pictures from my large AuSn platelets somewhere on 

Gregory's wall. If not, I can probably dig them up again from some old 

report. If such crystals are abundant in a solder joint, the components 

may just jump off the board when giving a mechanical shock.



/Inge



-----Ursprungligt meddelande-----

Från: TechNet [mailto:[log in to unmask]] För Werner Engelmaier /*

Skickat: den 16 januari 2008 20:30

Till: [log in to unmask]

Ämne: Re: [TN] SV: [TN] Solderability of Tin-Gold Intermetallic



Hi Inge,

As usual people are well advised not to argue with a (this) Swede; 1) he 

usually knows what he is talking about, and 2) if not, he will drink you 

under the table.

The IMCs formed by Sn/Pb, and Sn/Ag as well, are platellet-shaped crystals 

(in cross-section they may look like needles but are always plateletts), 

and I have seen no evidence that they are solderable. Solderability simply 

depends on how much Sn, or SnPb, to which you wet, is present. So the 

amount of these IMCs affect both solderability as well as 

Au/Ag-embrittlement.

Inge, how is Gerd? I sure have not heard anything about him for some time.







Werner







**************

Start the year off right.  Easy ways to stay in shape.

 

http://body.aol.com/fitness/winter-exercise?NCID=aolcmp00300000002489



---------------------------------------------------

Technet Mail List provided as a service by IPC using LISTSERV 15.0 To 

unsubscribe, send a message to [log in to unmask] with following text in the 

BODY (NOT the subject field): SIGNOFF Technet To temporarily halt or 

(re-start) delivery of Technet send e-mail to

[log in to unmask]: SET Technet NOMAIL or (MAIL) To receive ONE mailing per 

day of all the posts: send e-mail to

[log in to unmask]: SET Technet Digest

Search the archives of previous posts at: http://listserv.ipc.org/archives 

Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16

for additional information, or contact Keach Sasamori at [log in to unmask] or 

847-615-7100 ext.2815

-----------------------------------------------------



---------------------------------------------------

Technet Mail List provided as a service by IPC using LISTSERV 15.0 To 

unsubscribe, send a message to [log in to unmask] with following text in the 

BODY (NOT the subject field): SIGNOFF Technet To temporarily halt or 

(re-start) delivery of Technet send e-mail to [log in to unmask]: SET 

Technet NOMAIL or (MAIL) To receive ONE mailing per day of all the posts: 

send e-mail to [log in to unmask]: SET Technet Digest Search the archives of 

previous posts at: http://listserv.ipc.org/archives Please visit IPC web 

site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional 

information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 

ext.2815

-----------------------------------------------------



---------------------------------------------------

Technet Mail List provided as a service by IPC using LISTSERV 15.0

To unsubscribe, send a message to [log in to unmask] with following text in

the BODY (NOT the subject field): SIGNOFF Technet

To temporarily halt or (re-start) delivery of Technet send e-mail to 

[log in to unmask]: SET Technet NOMAIL or (MAIL)

To receive ONE mailing per day of all the posts: send e-mail to 

[log in to unmask]: SET Technet Digest

Search the archives of previous posts at: http://listserv.ipc.org/archives

Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 

for additional information, or contact Keach Sasamori at [log in to unmask] or 

847-615-7100 ext.2815

-----------------------------------------------------





---------------------------------------------------

Technet Mail List provided as a service by IPC using LISTSERV 15.0

To unsubscribe, send a message to [log in to unmask] with following text in

the BODY (NOT the subject field): SIGNOFF Technet

To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)

To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest

Search the archives of previous posts at: http://listserv.ipc.org/archives

Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815

-----------------------------------------------------



---------------------------------------------------------------------

This transmission (including any attachments) may contain confidential information, privileged material (including material protected by the solicitor-client or other applicable privileges), or constitute non-public information. Any use of this information by anyone other than the intended recipient is prohibited. If you have received this transmission in error, please immediately reply to the sender and delete this information from your system. Use, dissemination, distribution, or reproduction of this transmission by unintended recipients is not authorized and may be unlawful.



---------------------------------------------------

Technet Mail List provided as a service by IPC using LISTSERV 15.0

To unsubscribe, send a message to [log in to unmask] with following text in

the BODY (NOT the subject field): SIGNOFF Technet

To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)

To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest

Search the archives of previous posts at: http://listserv.ipc.org/archives

Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815

-----------------------------------------------------






ATOM RSS1 RSS2