Subject: silver migration
Author: Jos Groffils at Components-Evere
Date: 20-10-98 10:48
Hello,
We have done a lot of work on silver migration. Mostly one
thinks this is limited to humid conditions and direct
current.
However migration can als occur at high temperatures (> 200
degrees Celsius) under alternate current and is also
influenced by oxydising atmosphere as e.g. Sodium
Hypochlorite.
In litterature I don't find much information. Is someone
aware of studies, experience, tests, abstracts or
articles... about this subject?
Jos Groffils
---------------------------- Forwarded with Changes ---------------------------
From: Jos Groffils at Components-Evere
Date: 20/10/98 8:25AM
To: [log in to unmask] at #SMTP
Subject: silver migration
---------------------------- Forwarded with Changes ---------------------------
From: Jos Groffils at Components-Evere
Date: 16/10/98 10:32AM
To: [log in to unmask] at #SMTP
Subject: silver migration
---------------------------- Forwarded with Changes ---------------------------
From: Jos Groffils at Components-Evere
Date: 14/10/98 10:48AM
To: [log in to unmask] at #SMTP
Receipt Requested
Subject: silver migration
-------------------------------------------------------------------------------
################################################################
TechNet E-Mail Forum provided as a free service by IPC using LISTSERV 1.8c
################################################################
To subscribe/unsubscribe, send a message to [log in to unmask] with following text in the body:
To subscribe: SUBSCRIBE TechNet <your full name>
To unsubscribe: SIGNOFF TechNet
################################################################
Please visit IPC's web site (http://www.ipc.org) "On-Line Services" section for additional information.
For technical support contact Hugo Scaramuzza at [log in to unmask] or 847-509-9700 ext.312
################################################################
|
|
|