NO. ARE YOU PLATING Ag or Au, IN ORDER TO GET A BRIGHT SHINY DEPOSIT OF Ag
USING A Ni PRE-PLATE WILL REDUCE THE Ag THICKNESS REQUIRED; IF Au, THEN
BASEMETAL MIGRATION PREVENTION IS A CONCERN.
REGARDS,
LENNY KURUP
EMX ENTERPRISES LTD.
On Sat, 2 May 1998, GuitarBud wrote:
> I am plating stamped 1018-Steel parts with Ni and then Ag. I am then
> soldering them together with 2%Ag solder. It is roughly 1" x 8". Should I
> use Cu in place of the Ni?
>
> Frank
>
> ################################################################
> TechNet E-Mail Forum provided as a free service by IPC using LISTSERV 1.8c
> ################################################################
> To subscribe/unsubscribe, send a message to [log in to unmask] with following text in the body:
> To subscribe: SUBSCRIBE TechNet <your full name>
> To unsubscribe: SIGNOFF TechNet
> ################################################################
> Please visit IPC web site (http://jefry.ipc.org/forum.htm) for additional information.
> For the technical support contact Dmitriy Sklyar at [log in to unmask] or 847-509-9700 ext.311
> ################################################################
>
>
################################################################
TechNet E-Mail Forum provided as a free service by IPC using LISTSERV 1.8c
################################################################
To subscribe/unsubscribe, send a message to [log in to unmask] with following text in the body:
To subscribe: SUBSCRIBE TechNet <your full name>
To unsubscribe: SIGNOFF TechNet
################################################################
Please visit IPC web site (http://jefry.ipc.org/forum.htm) for additional information.
For the technical support contact Dmitriy Sklyar at [log in to unmask] or 847-509-9700 ext.311
################################################################
|
|
|