TECHNET Archives

February 1997

TechNet@IPC.ORG
Options: Use Monospaced Font
Show Text Part by Default
Condense Mail Headers

Message: [<< First] [< Prev] [Next >] [Last >>]
Topic: [<< First] [< Prev] [Next >] [Last >>]
Author: [<< First] [< Prev] [Next >] [Last >>]

Print Reply
Received:
by ipc.org (Smail3.1.28.1 #2) id m0vsFcb-0000gcC; Wed, 5 Feb 97 16:15 CST
Old-Return-Path:
<[log in to unmask]>
Date:
Wed, 5 Feb 1997 15:54:46 -0500 (EST)
Precedence:
list
Resent-From:
[log in to unmask]
Message-ID:
<[log in to unmask]>
X-Status:
Status:
O
From [log in to unmask] Fri Feb 7 14:
25:50 1997
TO:
[log in to unmask]
Return-Path:
<TechNet-request>
Resent-Message-ID:
<"bYjRU2.0.Y87.gOG-o"@ipc>
Subject:
Re: Low meelting point or temperature solder
From:
[log in to unmask]
X-Loop:
[log in to unmask]
X-Mailing-List:
<[log in to unmask]> archive/latest/9990
Resent-Sender:
TechNet-request [log in to unmask]
Parts/Attachments:
text/plain (26 lines) 
Hi Antoni,
Since I doubt that all the low melting solders you list as products of your
company are eutectic compositions, we would appreciate that Solidus and
Liquidus temperatures are given rather than a 'melting point' that most of
these solders do not really have.

Werner Engelmaier
Engelmaier Associates, Inc.
Electronic Packaging, Interconnection and Reliability Consulting
23 Gunther Street
Mendham, NJ  07945  USA
Phone & Fax: 201-543-2747
E-mail: [log in to unmask]

***************************************************************************
* TechNet mail list is provided as a service by IPC using SmartList v3.05 *
***************************************************************************
* To unsubscribe from this list at any time, send a message to:           *
* [log in to unmask] with <subject: unsubscribe> and no text.        *
***************************************************************************
* If you are having a problem with the IPC TechNet forum please contact   *
* Dmitriy Sklyar at 847-509-9700 ext. 311 or email at [log in to unmask]      *
***************************************************************************

ATOM RSS1 RSS2