LOL. I did live in Canada for 3 years when I was 19,20,21. Worked for Canada Telephone as a lineman, traveling all over the country, coast to coast, repairing phone lines. Lived up northeast of Flin Flon on a Cree Indian reservation. Best three years of my life; I never should have come home.
Odin
From: BEV CHRISTIAN [mailto:[log in to unmask]]
Sent: Thursday, April 26, 2018 7:16 PM
To: TechNet E-Mail Forum; Stadem, Richard D
Subject: RE: [TN] Flux question
đ I see you use âehâ. Part Canuck?
Bev
Sent from Mail<https://go.microsoft.com/fwlink/?LinkId=550986> for Windows 10
From: Stadem, Richard D<mailto:[log in to unmask]>
Sent: Thursday, April 26, 2018 1:19 PM
To: [log in to unmask]<mailto:[log in to unmask]>
Subject: Re: [TN] Flux question
Bev, you anwered at 12:17 my time, and I sent at 12:18 my time.
Then I read your response below.
Great minds think alike, eh?
-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of BEV CHRISTIAN
Sent: Thursday, April 26, 2018 12:17 PM
To: [log in to unmask]<mailto:[log in to unmask]>
Subject: Re: [TN] Flux question
Joey,
You probably donât want to hear this, but⊠the answer is âit dependsâ. How marginal is marginal? What is the lead finish? Are the pad connected to a ground plane? What is your reflow profile?
Regards,
Bev
Sent from Mail for Windows 10
From: Jose A Rios
Sent: Thursday, April 26, 2018 1:06 PM
To: [log in to unmask]<mailto:[log in to unmask]>
Subject: [TN] Flux question
Is ROL0 flux an adequate one when faced with having to solder marginally oxidized components. Or should a different flux type be selected. Application is ground based/hi-rel (non flight). Flowdown is J-001 (not space addendum). ThanksâŠ.