Thank you George! Our company had to stop processing OSP due to expense.
OSP is okay if you run alot of it. But, when the bath sets for days at a
time, the chemicals degrade. Replenishment/shelflife issues made it
prohibitively expensive.
At 07:39 AM 08/15/2005, you wrote:
>ENIG is the number one choice for a contacting surface.
>At the IPC Plating Committee round robin testing with ENIG as a contact
>surface indicated >1000,000 actuations without any change in resistivity.
>
>With good process control ENIG is free of "Black Pad" issues. The new IPC
>ENIG specifications 4553, that specifies less immersion gold (2-4 uins) has
>virtually eliminated BP.
>
>Do we stop using electroless copper because of occasional voiding, or inner
>layer separation?
>
>Do we stop using electrolytic copper because we occasionally have copper
>cracks?
>
>Do we stop etching because of oevr hang and undercut?
>
>PCB manufacturing is all about "PROCESS CONTROL"
>ENIG is no different.
>
>I agree that Immersion Silver has a lot of potential as a finish also.
>
>Best regards
>
>George Milad
>[log in to unmask]
>National Accounts Manager for Technology
>Uyemura International Corporation
>Technical Center
>240 Town LIne Rd
>Southington CT 06489
>(516) 901 3874 (mobile)
>(860) 793-4011 (office)
>(860) 793-4020 (fax)
>
>---------------------------------------------------
>Technet Mail List provided as a service by IPC using LISTSERV 1.8e
>To unsubscribe, send a message to [log in to unmask] with following text in
>the BODY (NOT the subject field): SIGNOFF Technet
>To temporarily halt or (re-start) delivery of Technet send e-mail to
>[log in to unmask]: SET Technet NOMAIL or (MAIL)
>To receive ONE mailing per day of all the posts: send e-mail to
>[log in to unmask]: SET Technet Digest
>Search the archives of previous posts at: http://listserv.ipc.org/archives
>Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16
>for additional information, or contact Keach Sasamori at [log in to unmask] or
>847-615-7100 ext.2815
>-----------------------------------------------------
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------
|
|
|