You need to re qual your assembly. You also need to check any components that max temp not allow to go over 230C. Check material compatibility for any used on assembly. Budget 30 to 50K in total (there is no guarantee it works after spending).
--------------------------
Sent using BlackBerry
----- Original Message -----
From: Mike Laroe [mailto:[log in to unmask]]
Sent: Monday, December 06, 2010 04:05 PM
To: [log in to unmask] <[log in to unmask]>
Subject: [TN] HandSoldering Using NC Solders
Currently my company has been using two different Alloys for handsoldering
both Leaded and RoHs No-Clean Assy's. For the leaded requirement we are
using AIM and for Rohs we are using Kester. We currently stock 4 different
sizes of each (.015", .020", .025", .031").. My question and thought is to
phase out the AIM and strictly only use the Kester for both Leaded and Rohs
Assy's. All the Soldering is done with Metcals using the 700 & Pwr Tips. Are
there any reasons I shouldn't do this?
Thanks for your help in advance,
Mike Laroe
Mfg Engineer
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------
---------------------------------------------------------------------
This transmission (including any attachments) may contain confidential information, privileged material (including material protected by the solicitor-client or other applicable privileges), or constitute non-public information. Any use of this information by anyone other than the intended recipient is prohibited. If you have received this transmission in error, please immediately reply to the sender and delete this information from your system. Use, dissemination, distribution, or reproduction of this transmission by unintended recipients is not authorized and may be unlawful.
______________________________________________________________________
This email has been scanned by the MessageLabs Email Security System.
For more information please contact helpdesk at x2960 or [log in to unmask]
______________________________________________________________________
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 15.0
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------
|
|
|