Mike Fenner <[log in to unmask]>
Content-Transfer-Encoding:
7bit
In-Reply-To:
Content-Type:
text/plain; charset="us-ascii"
MIME-Version:
1.0
Parts/Attachments:
text/plain (124 lines)
I would add

- slow cool down, this can give a coarser grain structure which can show as
dull/grainy.
- it's possible your component finish has changed (without notification is
not unknown) for Pb-free compliance.
- finally, disturbed joints of course, but I am sure you will have checked
that before coming on 'net.

Sometimes it a combination of things, so that if any one becomes marginal
the combined effect will tip you over.





Regards

Mike Fenner
Indium Corporation
We are at Productronica
click for details
www.indium.com/productronica/


-----Original Message-----
From: TechNet [mailto:[log in to unmask]] On Behalf Of David D. Hillman
Sent: 08 November 2005 19:22
To: [log in to unmask]
Subject: Re: [TN] Grainy Solder Joints

Hi Kevin! There are a number of metallurgical and microstructural reactions
that can result in a solder joint not having a "bright and shiny"
appearance. The majority of the time the lack of a "bright and shiny"
appearance results in absolutely no change in solder joint integrity. The
other minority instances, such as too much gold in a solder joint resulting
in a grainy appearance, the solder joint integrity is impacted. If you had
"bright and shiny" solder joint appearance before then something has changed
in your process - the change may not impact the solder joint integrity but
you should trace down what is now different. The use of Pbfree solder alloys
is going to make the "bright and shiny" solder joint appearance follow the
dinosaurs into extinction! JSTD-001 committee removed the "bright and shiny"
appearance criteria several years ago. The
IPC-HDBK-001 has some good information on "bright and shiny" that may be of
use.

Dave Hillman
Rockwell Collins
[log in to unmask]




             Kevin Glidden
             <[log in to unmask]
             COM>                                                       To
             Sent by: TechNet          [log in to unmask]
             <[log in to unmask]>                                          cc

                                                                   Subject
             11/08/2005 11:59          [TN] Grainy Solder Joints
             AM


             Please respond to
             [log in to unmask]
                    om






We are experiencing dull / grainy TH solder joints, made by hand soldering
w/ iron @ 500F.  At first, it appeared to be residue on the surface, so I
started chasing the cleaner.  But all checked out OK.  I refluxed (water
soluble, ORH0) and reflowed (iron @ 600F).  This improved the finished
appearance, but not 100%.  While eutectic, the joint is perfect.  Then when
I draw the iron away, it cools and the surface finish is no longer smooth or
shiny.  What can cause this?


---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e To
unsubscribe, send a message to [log in to unmask] with following text in the
BODY (NOT the subject field): SIGNOFF Technet To temporarily halt or
(re-start) delivery of Technet send e-mail to
[log in to unmask]: SET Technet NOMAIL or (MAIL) To receive ONE mailing per
day of all the posts: send e-mail to
[log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16
for additional information, or contact Keach Sasamori at [log in to unmask] or
847-615-7100 ext.2815
-----------------------------------------------------

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e To
unsubscribe, send a message to [log in to unmask] with following text in the
BODY (NOT the subject field): SIGNOFF Technet To temporarily halt or
(re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet
NOMAIL or (MAIL) To receive ONE mailing per day of all the posts: send
e-mail to [log in to unmask]: SET Technet Digest Search the archives of
previous posts at: http://listserv.ipc.org/archives Please visit IPC web
site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100
ext.2815
-----------------------------------------------------


***This email, its content and any files transmitted with it are intended solely for the addressee(s) and may be legally privileged and/or confidential. If you are not the intended recipient please delete and contact the sender by return and delete the material from any computer. Any review, retransmission, dissemination or other use of, or taking of any action in reliance upon, this information by persons or entities other than the intended recipient is prohibited.

Messages sent via this medium may be subject to delays, non-delivery and unauthorized alteration. This email has been prepared using information believed by the author to be reliable and accurate, but Indium Corporation makes no warranty as to accuracy or completeness. In particular, Indium Corporation does not accept responsibility for changes made to this email after it was sent. Any opinions or recommendations expressed herein are solely those of the author. They may be subject to change without notice.***

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------

ATOM RSS1 RSS2