You did not mention if your solder has been analyzed for contaminates. The
most troublesome contaminants are copper and gold. The following limits
should apply:
.25% for copper and .08% for gold. The combined total should not exceed
.30%.
Jan Satterfield
Edo Corp
Salt Lake City, UT
[log in to unmask]
----------
From: Terry Huddeston
To: dabonz; jasatt; Tech Net
Subject: ASSY: Gold contamination after wave sold
Original Subject:
ASSY: Gold contamination after wave soldering?
Could anyone out there help with the explaination of why after wave
soldering that there will appear a gold film mainly on top of the PWB?
Some of our inspectors are concerned and question what this substance
is?
Thanks for any help on this subject.
Terry Huddleston
Teledyne Lewisburg
***************************************************************************
* TechNet mail list is provided as a service by IPC using SmartList v3.05 *
***************************************************************************
* To unsubscribe from this list at any time, send a message to: *
* [log in to unmask] with <subject: unsubscribe> and no text. *
***************************************************************************
***************************************************************************
* TechNet mail list is provided as a service by IPC using SmartList v3.05 *
***************************************************************************
* To unsubscribe from this list at any time, send a message to: *
* [log in to unmask] with <subject: unsubscribe> and no text. *
***************************************************************************
|
|
|