Randy,
I have just dug the data out on these tests. Two cycles were run,
both were a 2hour cycle with 3.5C/min ramp rates, one -55 to +95C
and one -55 to +125C. Cracking in the +95 test was nearly as bad
as the +125 test, but no electrical failures occured for either
test regime.
David Whalley
Loughborough University
>
>What was the duration and ramp times on your 1812 capacitor tests?
> ----------
>From: TechNet-request
>To: TechNet
>Subject: Re: ASSY:FAB:Des: Joint Cracking LCCCC
>Date: Friday, September 13, 1996 11:45AM
>
>Bob,
>
>I have seen serious cracking in tests on 1812 capacitors in -55 to +125C
>test.
>They are a good bit smaller and the TCE mismatch not so bad so I am not at
>all surprised at what you are seeing.
>
>I would treat 1206's as the limit in kit that is going to see those sorts of
>temperatures (-55) regularly in service, unless measures are taken to reduce
>the problem.
>
>David Whalley
>
>
>>I have been looking at some 20 pin Leadless Ceramic Chip Carriers which
>have
>>exhibited cracks. They are mounted on standard FR4 and thermal cycled
>between
>>-55 +80 for 1000 hours.
>>
>>Cracking is a problem with this device as we know but not at these low lead
>>counts. Many uses in their design rules make 28 pin devices the limit and
>then
>>incorporate the use of matched substrate to reduce differential expansion.
>>
>>I would appreciate any feed back on failure that people have seen on
>testing
>of
>>low lead count devices or even feed back on where people see the limit on
>pin
>>count and the need for special substrates.
***************************************************************************