TECHNET Archives

December 2004

TechNet@IPC.ORG

Options: Use Monospaced Font
Show Text Part by Default
Condense Mail Headers

Message: [<< First] [< Prev] [Next >] [Last >>]
Topic: [<< First] [< Prev] [Next >] [Last >>]
Author: [<< First] [< Prev] [Next >] [Last >>]

Print Reply
Sender:
X-To:
TechNet E-Mail Forum <[log in to unmask]>, Edward Mines <[log in to unmask]>
Date:
Thu, 16 Dec 2004 13:44:59 -0500
Reply-To:
Subject:
From:
Joyce Koo <[log in to unmask]>
Content-Transfer-Encoding:
7bit
In-Reply-To:
Content-Type:
text/plain; charset="us-ascii"
MIME-Version:
1.0
Parts/Attachments:
text/plain (79 lines)
material compatiability study should not be done at production level.  Why
you are doing it on the populated board? If you done the work at front (in
the design stage as part of material selection), you should not see the need
to do it at production level.
Why?
                               jk

-----Original Message-----
From: TechNet [mailto:[log in to unmask]]On Behalf Of Edward Mines
Sent: Thursday, December 16, 2004 1:33 PM
To: [log in to unmask]
Subject: [TN] solder mask/conformal coating compatability


To the best of my knowledge there is no written standard for solder
mask/conformal coating compatability, but I have heard instances where poor
adhesion of conformal coating to the solder mask was preceived as a problem.
It's a dirty little secret that not all conformal coatings adhere to all
solder masks; I've seen some that peel right off, no matter how clean the
underling solder mask is.

At one time Enthione had a flier listing the "compatability" of popular
conformal coatings to their solder masks. THer criteria that they used to
judge this was vague. I don't know if it's still available.

HumiSeal tried to develop a correlation between the surface tensions of
conformal coatings and solder masks to predict adhesion but was
unsuccessful.

1B31S - a goosed up version of 1B31-  has improved adhesion to some problem
solder masks, but there are still some solder masks where 1B31S will  peel
right off.

Doug Pauls is correct that cleaning problems are sometimes mistaken for
incompatabilty of solder masks to conformal coating. Frequently this was
solder mask batch related, sometimes process, sometimes the chemistry of the
batch itself.

Somewhere IPC (IPC-CC-830?) calls out an adhesion test for conformal coating
to solder masks. The test cuts a grid larger than 1" X 1" into the coating
with a $100 plus apparatus and then trys to lift off coating squares with
tape. That test is  operator dependent (subjective) and it's hard to find a
1" square area free of components on most boards.



Edward Mines BEChE, MEChE
238 Willard Dr.
Hewlett, NY  11557
516 205-6523
__________________________________________________
Do You Yahoo!?
Tired of spam?  Yahoo! Mail has the best spam protection around

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to
[log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to
[log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16
for additional information, or contact Keach Sasamori at [log in to unmask] or
847-615-7100 ext.2815
-----------------------------------------------------
http://mail.yahoo.com

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------

ATOM RSS1 RSS2