Hello Phil,
For Sn/Pb alloy and ww flux we used to target PCB top temperature to
100-120°C max.
If you experienced insufficient hole filling, you may check also the
wave height.
Regards
Francesco
--
*Francesco Di Maio
*IPC e Formazione - IPC A-600,IPC A-610,IPC 7711/21 Certified IPC Trainer
SEM COMMUNICATION & GESTLABS srl
Il 02/11/2016 18:32, Stadem, Richard D. ha scritto:
> 125 to 150C has always worked well for me.
>
> -----Original Message-----
> From: TechNet [mailto:[log in to unmask]] On Behalf Of Nutting, Phil
> Sent: Wednesday, November 02, 2016 10:21 AM
> To: [log in to unmask]
> Subject: [TN] tin/lead wave solder profiles
>
> Hi all,
>
> It has become difficult to find information related to tin/lead wave soldering. We have a table top tin/lead wave solder system that we are having difficulty dialing in. We are running Kester 197 flux and Kester 63/37 bar solder and producing thru-hole circuit boards for space applications.
>
> I'm looking for typical 0.062" board parameters of top side board temperatures after fluxing and before hitting the wave.
>
> Thanks in advance,
>
> Phil Nutting | HVP Development Engineer | Excelitas Technologies Corp
>
> Lab: +1 978.224.4332 | Office: +1 978.224.4152
> 35 Congress St, Salem, MA 01970 USA
> [log in to unmask]<mailto:[log in to unmask]>
> www.excelitas.com<http://www.excelitas.com/>
>
>
> [Excelitas R_emailsig]
>
>
> Please consider the environment before printing this e-mail.
> ________________________________
> This email message and any attachments are confidential and proprietary to Excelitas Technologies Corp. If you are not the intended recipient of this message, please inform the sender by replying to this email or sending a message to the sender and destroy the message and any attachments. Thank you.
--
*Francesco Di Maio
*IPC e Formazione - IPC A-600,IPC A-610,IPC 7711/21 Certified IPC Trainer
SEM COMMUNICATION & GESTLABS srl
e-mail: [log in to unmask]
//
|
|
|