I don't have the spec available but I would think that Palladium finish in a
gold socket would be fine. I would not want to solder directly to Palladium
however. Maybe Dave ( the guy who cuts up water pipes from his house! ) could
give us some insight.
-----Original Message-----
From: - Bogert [mailto:[log in to unmask]]
Sent: Friday, 25 February 2005 5:06 PM
To: [log in to unmask]
Subject: [TN] Microcircuit Palladium Lead Finish (Good or Bad)?
February 25, 2005
MIL-PRF-38535 microcircuit specification is confusing since in one section it
identifies that to select a lead finish, include a suffix letter as part of
the part number. The available suffix letters are Finish "A", "B", "C":, "D"
and "X". "D" is for Palladium. "X" means either "A", "B", or "C" Finish
However, Appendix A of the specification indicates that only lead Finishes
"A" through "C" (or "X") are allowed.
It appears that Finish "D", Palladium finished microcircuit leads are not
allowed. Is this true? If so, why the apparent prohibition on Palladium
lead finish?
The question relates to selecting the lead finish for a microcircuit that is
mounted in a socket having Gold-plated socket contacts. Normally, one should
specify a Gold-plated microcircuit lead (Finish "C") to mate with the
Gold-plated socket contact. However, from a galvanic corrosion standpoint,
either Gold or Palladium should be ok.
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to
[log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to
[log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16
for additional information, or contact Keach Sasamori at [log in to unmask] or
847-615-7100 ext.2815
-----------------------------------------------------
---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------
|
|
|