Hi folks! Let's look at some numbers! The thermal conductivity (in W/ m K
in the 0-100C range) is 237 for Al, 318 for Au and 66.8 for Sn. You should
have better heat transfer by going way from Sn - but as Brian described the
thermal transfer game is ruled by surface contact. Brian also mentioned the
issue/question of galvanic compatibility, the same question I queried the
TechNet community on several weeks back. I received a number of good
information leads but nothing as definitive as I was looking to obtain.
Here is an update to that question - I began a series of tests: the
silver/aluminum and gold/aluminum galvanic couples test vehicles (circuit
boards with the appropriate finishes coupled to Al casings by Al standoffs
and having a 5 volt bias) have completed 250 hours of 85C/85%RH with no
issues of galvanic compatibility! The salt fog tests begin next week and
I'll keep everyone updated as those tests progress. It appears that the
anode-to-cathode relationship is a key parameter in equation.
Dave Hillman
Rockwell Collins
[log in to unmask]
Brian Ellis
<b_ellis@PROTONIQ To: [log in to unmask]
UE.COM> cc:
Sent by: TechNet Subject: Re: [TN] Heat transfer from ENIG board to aluminium casing
<[log in to unmask]>
03/18/2003 06:54
AM
Please respond to
"TechNet E-Mail
Forum."; Please
respond to Brian
Ellis
Daan
I would have thought exactly the opposite! An uneven HASL surface will
have fewer contact points to the aluminium than a flat ENIG surface.
That having been said, I would have thought that both would be bad,
electrochemically speaking, if subjected to humidity. From very poor
memory, the Al-Au couple is somewhere about 4 V, roughly double that of
Al-Sn/Pb.
Brian
d. terstegge wrote:
> Hi Technet,
>
> We are in the process of converting some of our boarddesigns from HASL
> to ENIG conductor finishing. Now one of our designers is worried about
> the effect that this change may have on heat transfer from the plated
> board-edges to the aluminium casing on which the board is mounted. He
> feels that the heattransfer from leadtin to aluminium is better that for
> nickel/gold to aluminium, possibly resulting in heat problems in the end
> product.
>
> Any ideas on this ?
>
> Daan Terstegge
> Thales Communications
> Unclassified mail
> Personal Website: http://www.smtinfo.net
>
> ---------------------------------------------------
> Technet Mail List provided as a free service by IPC using LISTSERV 1.8e
> To unsubscribe, send a message to [log in to unmask] with following text in
> the BODY (NOT the subject field): SIGNOFF Technet
> To temporarily halt or (re-start) delivery of Technet send e-mail to
[log in to unmask]: SET Technet NOMAIL or (MAIL)
> To receive ONE mailing per day of all the posts: send e-mail to
[log in to unmask]: SET Technet Digest
> Search the archives of previous posts at:
http://listserv.ipc.org/archives
> Please visit IPC web site http://www.ipc.org/html/forum.htm for
additional
> information, or contact Keach Sasamori at [log in to unmask] or 847-509-9700
ext.5315
> -----------------------------------------------------
>
>
>
---------------------------------------------------
Technet Mail List provided as a free service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to
[log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to
[log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/html/forum.htm for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-509-9700
ext.5315
-----------------------------------------------------
---------------------------------------------------
Technet Mail List provided as a free service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/html/forum.htm for additional
information, or contact Keach Sasamori at [log in to unmask] or 847-509-9700 ext.5315
-----------------------------------------------------
|
|
|