Dewey, what finish alloys use up to 3% Bi?
Genny, what indications have you seen that the EU may eventually want to ban
Bi?
> -----Original Message-----
> From: Leadfree [mailto:[log in to unmask]] On Behalf Of
> Whittaker, Dewey (AZ75)
> Sent: Thursday, January 06, 2005 10:30 AM
> To: [log in to unmask]
> Subject: Re: [LF] The use of Bismuth
>
>
> We are seeing components with this finish. There is data to
> support the acceptability of a final lead finish containing
> up to 3% Bismuth. Dewey
>
> -----Original Message-----
> From: Leadfree [mailto:[log in to unmask]]On Behalf Of Genny Gibbard
> Sent: Thursday, January 06, 2005 9:15 AM
> To: [log in to unmask]
> Subject: [LF] The use of Bismuth
>
>
> So I am curious, what are people thinking about the use of
> bismuth in lead free termination finishes. I am not talking
> about solder containing Bi. The only supplier I have come
> across so far specifically mentioning they use Bi is NEC.
> They have a doc on their website, called "Japan's best kept
> secret" http://www.cel.com/pdf/marcomnews/japan_best.pdf
> that claims
> that SnBi is recommended by JEITA, as opposed to the
> recommendation of JEDEC for Matte Sn. They make it sound as
> if a lot of companies are using this plating, but I haven't
> come across any other components so far that use it. The main
> concern I have is that I keep getting the impression that the
> next metal that the EU will be gunning for eliminating is Bi,
> so it doesn't sound like a smart direction to go.
>
> Thoughts?
>
> Genny Gibbard (mailto:[log in to unmask])
>
> --------------------------------------------------------------
> --------------
> ---Leadfee Mail List provided as a service by IPC using
> LISTSERV 1.8d To unsubscribe, send a message to
> [log in to unmask] with following text in the BODY (NOT the
> subject field): SIGNOFF Leadfree To temporarily stop/(start)
> delivery of Leadree for vacation breaks send: SET Leadfree
> NOMAIL/(MAIL) Search previous postings at:
> http://listserv.ipc.org/archives Please visit IPC web > site
> http://www.ipc.org/contentpage.asp?Pageid=4.3.16
> for additional information, or contact Keach Sasamori at
> [log in to unmask] or 847-615-7100 ext.2815
> --------------------------------------------------------------
-------------------------------------------------------------------------------Leadfee Mail List provided as a service by IPC using LISTSERV 1.8d
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Leadfree
To temporarily stop/(start) delivery of Leadree for vacation breaks send: SET Leadfree NOMAIL/(MAIL)
Search previous postings at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-------------------------------------------------------------------------------
|
|
|