Hi,Vincent,
You can try to use double solder wave. the chip solder should be high!
Best Regards
Qu Zenglong
Industrial Engineering Department
Production Division
BISC, China
Tel: 0086-10-64346323
Fax:0086-10-64367731
e-mail: [log in to unmask]
----------
From: Vincent BADA[SMTP:[log in to unmask]]
Reply To: TechNet E-Mail Forum.;Vincent BADA
Sent: Thursday, September 30, 1999 2:32 PM
To: [log in to unmask]
Subject: [TN] Wave soldering
Sensitivity: Confidential
Hi all,
What is the minimum vertical fill of solder for plated through holes ?
We have some problems to obtain the 75% requested by IPC-A-610 for a class 2
board.
In fact, the board has a thickness of 3,2 mm.
We use a no-clean flux and the wave is under nitrogen.
Is there any special criteria regarding to the thickness of the board ?
Has anyone succeeded in obtaining a correct solder filet for thick boards ?
Thanks,
Vincent Bada
Process Engineer
Alcatel Etca
Charleroi
Belgium
##############################################################
TechNet Mail List provided as a free service by IPC using LISTSERV 1.8c
##############################################################
To subscribe/unsubscribe, send a message to [log in to unmask] with following text in
the body:
To subscribe: SUBSCRIBE TECHNET <your full name>
To unsubscribe: SIGNOFF TECHNET
##############################################################
Please visit IPC web site (http://www.ipc.org/html/forum.htm) for additional
information.
If you need assistance - contact Gayatri Sardeshpande at [log in to unmask] or
847-509-9700 ext.5365
##############################################################