Hello fellow Blaser (Laser), There are more "experts" on laser drilling than there are lasers out there (if you get my drift). Some basic facts help with this strategy. The ablation rate is a combination of energy and time. If you review the graphs pertaining to CO2 or UV/Yag you will see that in the UV systems there is a large variance between glass and resin, but in CO2 there curves are closer. If you can live with the print/laser registration issues CO2 may be your best bet. My issues with FR-4 ablation are as follows: 1. Using a UV/Yag system the alignment is excellent, but the sidewall is not smooth. This can be a real problem when trying to produce vias with aspect ratios > .5 (dielectric) to 1 (Top Dia. of hole). Look at the weave pattern of both 2313 and 106, neither is completely uniform. If you look at hundreds of holes at a time you'll see large variations from your "optimum hole" to your "worst hole". Also in Lasering the vias the spot size of the spiral cycle must be small enough to overlap without creating the classic copper finger in the capture pad which causes partial voids during plating. Double cycling is recommended for this. Even a third trepan cycle helps (the suppliers don't recommend this because the throughput numbers stink!). The vias/ sec. are about 10 (ugh!). 2. Using C02 the holes are ablated at a more even rate. They require a pre-etch process unless you are using very thin copper (we haven't had much success with the thin copper either). Registration is critical as you will ablate right past the pad if misaligned. Also the heat created from this process causes a "ash" at the base of the hole that needs plasma removal. Once all of these steps are done the hole looks more like at football than a tea cup. You didn't ask, but I tell you anyway.... I'd run 1 ea. of 106 and use RCC with a UV/Yag. The RCC resins are UL approved and are FR-4 materials. Hope this helps, Joe Dickson Dir. of Engineering Tyco Intl. Santa Clara, Ca. [log in to unmask] > I have a product that requires a .006 dia. laser ablated via from > lyr 1 to 2. I'm required to use glass re-inforced FR-4 as a > dielectric. The dielectric is approx .0035. I can either use a > single ply of 2313 or 2 plies of 106 prepreg. Which would be the > most favorable construction in terms of laser hole quality and > subsequent processing? >