Connie, your plating situation will depend on the actual circuit layout and density on your pwb. If you have many isolated traces, then you will have difficulty with over plating. You may want to try sheilding of the anodes(to redirect some of the current), reduce your cathode current density, increase acid concentration, reduce copper concentration, reduce anode area, and/or try pulse plating. Good luck -----Original Message-----iel- LYPME <[log in to unmask]>