Dear Pacrim,

You did not mention if the boards in question are HASL, bare copper(OSP)
or reflowed tin-lead. It could be that there is a contamonated base metal
surface for many reasons, plated alloy of tin-lead deviating
significantly from the eutectic or poor plating distribution leading to
thin plating.

Good luck

################################################################