I have a customer who is concerned about Ionic contamination due to bromines/bromides. I have explained to the customer that the flame retardant in FR-4 material is based on bromine. Also, the flux that we use for the HAL is Hydrobromic Acid based, this is used instead of Hydrochloric Acid based flux to cut down on the chloride contamination. If anyone has information concerning this subject, I would appreciate any and all information. I can be contacted at: Scott Foley Environmental & Process Manager Ozark Circuits, Inc. 933 W. Chase Springfield, Missouri 65803 Phone: 417-864-5004 Fax: 417-864-4072 email: [log in to unmask] ################################################################ TechNet E-Mail Forum provided as a free service by IPC using LISTSERV 1.8c ################################################################ To subscribe/unsubscribe, send a message to [log in to unmask] with following text in the body: To subscribe: SUBSCRIBE TechNet <your full name> To unsubscribe: SIGNOFF TechNet ################################################################ Please visit IPC's web site (http://www.ipc.org) "On-Line Services" section for additional information. For technical support contact Hugo Scaramuzza at [log in to unmask] or 847-509-9700 ext.312 ################################################################