higher temperature solder pot will increase build up of copper much faster which leads to contaminated solder. -----Original Message----- From: Todd Ness <[log in to unmask]> To: [log in to unmask] <[log in to unmask]> Date: Tuesday, June 30, 1998 3:11 PM Subject: [TN] Wave Solder Pot Temp-63/37 Hi, I would like to know the differences between having our solder pot temp for 63/37 solder at 261 Degrees C instead of 250 Degrees C. Will we see less bridging and better top-side flow at the higher temp? Are there any pros and cons for the different temperatures? Thanks, Todd N ################################################################ TechNet E-Mail Forum provided as a free service by IPC using LISTSERV 1.8c ################################################################ To subscribe/unsubscribe, send a message to [log in to unmask] with following text in the body: To subscribe: SUBSCRIBE TechNet <your full name> To unsubscribe: SIGNOFF TechNet ################################################################ Please visit IPC web site (http://jefry.ipc.org/forum.htm) for additional information. For technical support contact Hugo Scaramuzza at [log in to unmask] or 847-509-9700 ext.312 ################################################################ ################################################################ TechNet E-Mail Forum provided as a free service by IPC using LISTSERV 1.8c ################################################################ To subscribe/unsubscribe, send a message to [log in to unmask] with following text in the body: To subscribe: SUBSCRIBE TechNet <your full name> To unsubscribe: SIGNOFF TechNet ################################################################ Please visit IPC's web site (http://www.ipc.org) "On-Line Services" section for additional information. For technical support contact Hugo Scaramuzza at [log in to unmask] or 847-509-9700 ext.312 ################################################################