Hi Scott,
    Hmmmmmmmmmm..  Interesting scenario.  I need to ask a couple of obvious questions first.
    Is the copper equal on both sides BEFORE You run the boards through the the soldering
process?
    Does the top side contain heavy shield as opposed to the bottom side?  If so, then you have a
low current density area that is not plating both sides equally.
    If not, Then the plating anode placement is out of whack.
This is a tough question to answer without a lot more detail.  If you Email me, I can Talk some
more detail.  JOHN WAITE

Scott M. Severson wrote:

> Hi All,
>
> Another question for who can ever answer it.
>
> What factors affect the dissolution of plated copper into solder during the
> soldering process?  Lets ignore the soldering parameters (temperature,
> composition, wave/pot turbulence....) and focus on the copper plating.
>
> We have PCBs that are seeing a 50% reduction in plated copper thickness
> during a standard IPC TM-650 thermal stress.  We've cross-sectioned enough
> thermal stressed boards to know that this isn't normal.   Another question.
>  We are consistently seeing the reduction on the top side of the board (the
> side that doesn't come in direct contact with the molten solder), why the
> top side and not the solder side?
>
> The boards are 14 layer with 4 2oz copper power/ground planes.
>
> Thanks
>
> Scott Severson
> Benchmark Electronics Inc.
>
> ################################################################
> TechNet E-Mail Forum provided as a free service by IPC using LISTSERV 1.8c
> ################################################################
> To subscribe/unsubscribe, send a message to [log in to unmask] with following text in the body:
> To subscribe:   SUBSCRIBE TechNet <your full name>
> To unsubscribe:   SIGNOFF TechNet
> ################################################################
> Please visit IPC web site (http://jefry.ipc.org/forum.htm) for additional information.
> For the technical support contact Dmitriy Sklyar at [log in to unmask] or 847-509-9700 ext.311
> ################################################################

################################################################
TechNet E-Mail Forum provided as a free service by IPC using LISTSERV 1.8c
################################################################
To subscribe/unsubscribe, send a message to [log in to unmask] with following text in the body:
To subscribe:   SUBSCRIBE TechNet <your full name>
To unsubscribe:   SIGNOFF TechNet 
################################################################
Please visit IPC web site (http://jefry.ipc.org/forum.htm) for additional information.
For the technical support contact Dmitriy Sklyar at [log in to unmask] or 847-509-9700 ext.311
################################################################