---------- From: Denis Meloche[SMTP:[log in to unmask]] Sent: Thursday, April 10, 1997 2:58 PM To: Baker,Kelly Subject: Electroless Gold Dennis, Thanks for your help, but its immersion gold that were using. Any information that you have for this would be greatly appreciated. Thanks again, Kelly I have specified and used electroless gold platings for mil-std for a number of years. I remember that there were specifications which allowed my previous employer to waive solder tining requirement if the Au was between a range of thicknesses. We ended using Au for a number of applications where tinning was impractical. I don't remember the specification we used. I still have email access to my old employer and could probably get you an answer in a few days. I also have the email address for our old DCAS inspector and he knew the spec # for everything. If you need any soldering help for Au I have a publication from the international tin institute I could send you. Good Luck, Denis Meloche Technical Sales Engineer Heraeus Cermalloy Division 24 Union Hill Rd West Conshohocken Pa., 19428 610-825-6050 Fax 610-825-7061 E-Mail [log in to unmask] *************************************************************************** * TechNet mail list is provided as a service by IPC using SmartList v3.05 * *************************************************************************** * To subscribe/unsubscribe send a message <to: [log in to unmask]> * * with <subject: subscribe/unsubscribe> and no text in the body. * *************************************************************************** * If you are having a problem with the IPC TechNet forum please contact * * Dmitriy Sklyar at 847-509-9700 ext. 311 or email at [log in to unmask] * ***************************************************************************