Dave, None of these boards have legend markings but your comments are helpful. I no longer have the boards here but as I recall, they were worse in one direction. As for which end of the pad, the most pronounced areas were on the outside edges away from the component package, but as you point out, the other end was hidden under the component. I don't recall if they were typically worse along one leading edge. The most popular replies so far have been in favor of attributing the problem to improper cleaning/solution entrapment around the soldermask boarder. All inputs considered, the problem could be a combination of both cleaning and intermetallics. All the boards in question were leveled using horizontal HASL and all have solder mask dams between the pads.The solder thickness on the pads would be thinner in one direction over the other. I expect this will happen again, since nothing has been changed. When it does occur I will take a closer look for patterns and keep better notes. Thanks for your input. Norm Dill ---------- From: TechNet-request To: Technet Subject: Re: FW: ASSY: Fine Pitch Dewetting? Date: Tuesday, April 30, 1996 12:26AM Is it possible that you have an intermettalic growth on the end of the fine pitch SMD pad? Is it possible that these boards have backprint (aka legend, marking matrix, etc.)? If so, it may be a phenomenon of the baking after HASL (assuming your supplier applies after solder mask). In my experience, in fine pitch SMD applications with backprint, the registration of the ink is super critical. This results in a lot of setup and perhaps misprints requiring rework (this could also be a cause of this problem), forcing the supplier to apply backprint after HASL to minimize ink on copper problems. The additional thermal abuse that the SMD pads experience in order to cure the ink applied can cause intermettalic growth. This would explain the observances listed in your message. This intermettalic is explained by the natural thin solder deposit resulting in the "leading edge" of the pad in the HASL air knives. If so, the problem would be more pronounced on the opposite ends of the SMD quad device pads, visually I would expect to see this problem on the outside of one end of the fine pitch pads, while on the inside end of the opposite pads of the same orientation (or vice versa). You would not be able to see the inside problem due to the device itself. I would also expect to see very little problem, if at all, on the other pads that are perpendicular to the pads exhibitig the problem. I am curious to see if this makes sense. Dave Rooke __________ reply separator _______________ >Rudy, > Because it was confined to the fine pitch areas, there may be a >connection to residues but if the problem was solder mask residues, wouldn't >the result be "non-wetting" with some visible areas of exposed copper? > These boards were HASL'd by the supplier and they looked just fine. > After they went through our IR process, some of the fine pitch pads do not >stay fully wet with solder. No exposed copper can be seen, but on some of >the finished solder connections ~20 - 30% of the pad surface refuses to >allow the new solder to flow onto it. Generally these areas are from the >outside of the pads inward. None were in the middle of the pad. > At this point, I'm open to suggestions. > > Norm Dill > [log in to unmask] > ---------- >From: TechNet-request >To: TechNet >Subject: Re: ASSY: Fine Pitch Dewetting? >Date: Thursday, April 25, 1996 11:19AM > >Is it possible that the problem is coming from soldermask residues that the >developer did not remove?? This would account for it not occuring in large >pad areas, as the developer may have trouble getting into the very small >areas. > >Rudy Sedlak >RD Chemical > > ----------------------------- Original Post -------------------- > Recently we have seen dewetting (~20 to 30%) that appears only on some >of the fine pitch pads. Larger pads with various components on the same >boards are ok. This has been seen on HASL boards from two different >suppliers. There have been no reports of problems with our regular daily >production lots. > Any opinions would be welcomed. > > > D. Rooke ([log in to unmask])