---------- From: [log in to unmask] To: [log in to unmask] Subject: ASSY: Peelable Soldermask for Wave Soldering Process Date: Monday, November 18, 1996 4:23PM Dale We are using and have been using a UV curable - peelable solder mask for about 3 years now with very good results the maskant we are using is Dymax 945 with a conveyorized UV light source. Our typical cure time is 15-20 sec. The only negative to this product is that it does leave a slight stain on fr4 with or without soldermask. Daugherty, Dale @JOCY (@JOCY") Thu, 14 Nov 1996 16:16:00 -0500 Messages sorted by: [ date ][ thread ][ subject ][ author ] Next message: [log in to unmask]: "Re: FAB: Finding a Solderpot" Previous message: Dwight Matti: "ARRGHH! Re: Silver Ink Screen Print." From: "Daugherty, Dale @JOCY" <[log in to unmask]> To: Internet - IPC TechNet <[log in to unmask]> I am looking for information on peelable soldermask used prior to wave soldering. We currently use Alpha 110 and must allow 3-4 hours drying time on thicker areas. 1) What peelable mask do you use and how much time must you allow for it to dry before you can run it through the wave? 2) Does anyone have experience with UV curable mask? Dale Daugherty [log in to unmask] (423) 461-2228 *************************************************************************** * TechNet mail list is provided as a service by IPC using SmartList v3.05 * *************************************************************************** * To unsubscribe from this list at any time, send a message to: * * [log in to unmask] with <subject: unsubscribe> and no text. * *************************************************************************** *************************************************************************** * TechNet mail list is provided as a service by IPC using SmartList v3.05 * *************************************************************************** * To unsubscribe from this list at any time, send a message to: * * [log in to unmask] with <subject: unsubscribe> and no text. * ***************************************************************************