Subject: Time:9:22 AM OFFICE MEMO Insp. of Low Residue Hd. Soldering Date:9/25/95 We are about to implement a low residue hand soldering operation in a military application. With customer permission, the flux residue from low residue soldering will not be considered a MIL-STD-2000A defect. We must transition from an inspection philosophy that considers all flux residues a defect to one that allows flux residues from low residue soldering. We need to re-train inspectors and re-write inspections procedures to accomodate the change. Before we go down the path of trying to verbalize the visual differences between acceptable flux residues and unacceptable flux residues, I thought I might look to TechNet. Are there folks out there with experience to share on this subject? Your help would be greatly appreciated. Mary Davis [log in to unmask]