Eli,

ENiG vias will ICT just fine.  The only reason to add solder would be to plug 
the holes if you want to keep the probes out, or to aid vacuum.  But you're 
generally better off not adding unneccesary solder to a board.  We haven't 
needed to change anything in our ICT processes for RoHS materials.

Pete

---------------------------------------------------