As the world is moving fast to LF components only, we will need to Reballing or Replating the components on a regular base. It seems that the mix technology at my company will continue for a few years. 1. Can you suggest me on a company that give these services, preferably a company that works with the Aerospace industry? 2. We decided to replate gull wing components (Pure tin plated) with a pitch smaller then 0.65 mm? Does this decision make sense as a tin whisker mitigation, what other Aerospace company do? Thanks and regards, Dr. Gil Zilber Technologist, Elta system Ltd. Tel. +972-8-8577240 Mobile +972-54-4983222 http://www.iai.co.il/site/en/iai.asp?pi=17887 The information contained in this communication is proprietary to Israel Aerospace Industries Ltd., ELTA Systems Ltd. and/or third parties, may contain classified or privileged information, and is intended only for the use of the intended addressee thereof. If you are not the intended addressee, please be aware that any use, disclosure, distribution and/or copying of this communication is strictly prohibited. If you receive this communication in error, please notify the sender immediately and delete it from your computer. Thank you. This message is processed by the PrivaWall Email Security Server. --------------------------------------------------- Technet Mail List provided as a service by IPC using LISTSERV 15.0 To unsubscribe, send a message to [log in to unmask] with following text in the BODY (NOT the subject field): SIGNOFF Technet To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL) To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest Search the archives of previous posts at: http://listserv.ipc.org/archives Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815 -----------------------------------------------------