Hi Bev, The AuSn platelets do not stop the wetting to the rest of the surface. The AuSn platelets are not likely to disolve in a soldering process. If there is too muc mof a concentration, they are likely to cause Au-embrittlement problems. Werner ************** Start the year off right. Easy ways to stay in shape. http://body.aol.com/fitness/winter-exercise?NCID=aolcmp00300000002489 --------------------------------------------------- Technet Mail List provided as a service by IPC using LISTSERV 15.0 To unsubscribe, send a message to [log in to unmask] with following text in the BODY (NOT the subject field): SIGNOFF Technet To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL) To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest Search the archives of previous posts at: http://listserv.ipc.org/archives Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815 -----------------------------------------------------