Hi Netters,

I am wondering if the last months shed more light on how the various alloys perform. I have skimmed the report recommended by Dave Hillman, available at http://www.acqp2.nasa.gov/LFS.htm but cannot see a clear recommendation.

My stock of SAC305 solder bar is almost depleted and I have to make a decision: shall I continue with SAC305, or switch to SN100C or SACX?

Beyond the cosmetics of the joints and the maintainability of the solder pot, what is your feedback on reliability? Since I am running SAC305 paste, if I use a different alloy at wave, shall I expect more trouble than having the same SAC305 in both processes?

Thanks,

Ioan

 

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------