Happy Friday Everyone, Since we had our Friday earlier this week I guess I'll ask a straight question. We are currently soldering with SN63 and are getting more and more lead free parts. We have created a list of lead finishes that we believe work OK in our tin/lead process. This morning we got a notice from a component supplier that they will be switching to SN96AG4. Have any of you had experience soldering this lead finish with SN63? Have you done any testing of this combination? Thanks, KennyB --------------------------------------------------- Technet Mail List provided as a service by IPC using LISTSERV 1.8e To unsubscribe, send a message to [log in to unmask] with following text in the BODY (NOT the subject field): SIGNOFF Technet To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL) To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest Search the archives of previous posts at: http://listserv.ipc.org/archives Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815 -----------------------------------------------------