Hi Werner, I don't think there is a significant difference between the Klein-Wassink numbers (which are given in um/sec.) and Wally's data which I gave in u"/sec. Regards, George George M. Wenger, Andrew Corporation Reliability / FMA Engineer Base Station & Subsystems Group 40 Technology Drive, Warren, NJ 07059 (908) 546-4531 [log in to unmask] -----Original Message----- From: [log in to unmask] [mailto:[log in to unmask]] Sent: Monday, August 22, 2005 11:41 PM To: Wenger, George M.; [log in to unmask] Subject: Re: [TN] max thickness electroplated gold Hi George, I use Klein-Wassink as my source; according to his data, the data you quote are somewhat high. Maybe the graph below is useful. Werner ------------------------------------------------------------------------------------------------ This message is for the designated recipient only and may contain privileged, proprietary, or otherwise private information. If you have received it in error, please notify the sender immediately and delete the original. Any unauthorized use of this email is prohibited. ------------------------------------------------------------------------------------------------ --------------------------------------------------- Technet Mail List provided as a service by IPC using LISTSERV 1.8e To unsubscribe, send a message to [log in to unmask] with following text in the BODY (NOT the subject field): SIGNOFF Technet To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL) To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest Search the archives of previous posts at: http://listserv.ipc.org/archives Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815 ----------------------------------------------------- [mf2]