I am looking for a conformal coating that can withstand the use of a
cleaner (Lixton TS-974)
We have a customer who uses our parts that are coated with Humiseal 1A33
and is cleaning them in an ultrasonic cleaner that has Lixton TS-974 in it.
They are complaining that the coating is coming off.  With the ingredients
I see below there is no wonder.   So my first question was, is there a
conformal coating that will withstand this material or if not is there a
better cleaner I could recommend that will not remove the humiseal.
Remember it has to go into an ultrasonic cleaner.

Thank in advance.


The ingredients are in this material are:
LIXTON

50 - 10%    4-Hydroxy-4-methyl-pentan-2-0n
2.5 - 10%   N-methyl-2-pyrrolidome
2.5%           Alkylaminethoxylat
2.5%           modifiziertes Fettalkoholetethoxylat




STATEMENT OF CONFIDENTIALITY:

If you have received this e-mail in error, please immediately notify the
sender by e-mail at the address shown.  This e-mail and any attachments may
contain confidential information. This information is intended only for the
use of the individual(s) or entity to whom it is intended even if addressed
incorrectly.  Please delete it from your files if you are not the intended
recipient.  Thank you for your compliance.

---------------------------------------------------
Technet Mail List provided as a service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in
the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/contentpage.asp?Pageid=4.3.16 for additional information, or contact Keach Sasamori at [log in to unmask] or 847-615-7100 ext.2815
-----------------------------------------------------