I have seen this problem and it turned out to be a reaction between the flux
and the "anti-drossing" agents in the solder bar.  I can't remember the brand,
but changing to a good grade of Sn63 bar without the additives got rid of the
problem completely.



Jon Moore

---------------------------------------------------