Barbara,
Welcome.
 
I do not understand you question, as stated.  Are you sure you meant to put 125C?!  Eutectic tin/lead solder melts at 183C.
 
Also, make sure you check out the archives, mentioned below.  It helps you avoid asking questions we have seen a zillion times.  This one, as stated, is new, though.
regards,
Bev Christian
Research in Motion
-----Original Message-----
From: Rich, Barbara J [mailto:[log in to unmask]]
Sent: July 17, 2003 1:12 PM
To: [log in to unmask]
Subject: [TN] no clean

Hi all,

I am new to this forum and would like to know if there is any literature stating that no clean solder needs to be heat activated to 125 degrees C.?

 

 

 

---------------------------------------------------
Technet Mail List provided as a free service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/html/forum.htm for additional information, or contact Keach Sasamori at [log in to unmask] or 847-509-9700 ext.5315
-----------------------------------------------------
---------------------------------------------------
Technet Mail List provided as a free service by IPC using LISTSERV 1.8e
To unsubscribe, send a message to [log in to unmask] with following text in the BODY (NOT the subject field): SIGNOFF Technet
To temporarily halt or (re-start) delivery of Technet send e-mail to [log in to unmask]: SET Technet NOMAIL or (MAIL)
To receive ONE mailing per day of all the posts: send e-mail to [log in to unmask]: SET Technet Digest
Search the archives of previous posts at: http://listserv.ipc.org/archives
Please visit IPC web site http://www.ipc.org/html/forum.htm for additional information, or contact Keach Sasamori at [log in to unmask] or 847-509-9700 ext.5315
-----------------------------------------------------